s20nm_l600nm_1																
strain_X [-]	stress_X [MPa]	strain_Y [-]	stress_Y [MPa]	strain_Z [-]	stress_Z [MPa]											
	0.00000			0.000			0.00000			0.000			0.00000			0.000
	0.00055			0.540			0.00055			0.582			0.00056			0.529
	0.00111			1.079			0.00111			1.163			0.00112			1.055
	0.00194			1.880			0.00194			2.030			0.00195			1.838
	0.00319			3.045			0.00319			3.288			0.00321			2.990
	0.00506			4.678			0.00506			4.999			0.00509			4.602
	0.00787			6.765			0.00787			7.114			0.00792			6.585
	0.01067			8.369			0.01067			8.682			0.01216			8.642
	0.01348			9.587			0.01348			9.829			0.01774			10.267
	0.01769			10.907			0.01769			11.043			0.02333			11.238
	0.02323			12.081			0.02323			12.097			0.02891			11.872
	0.02878			12.882			0.02878			12.790			0.03450			12.318
	0.03432			13.461			0.03432			13.276			0.04008			12.651
	0.03987			13.900			0.03987			13.639			0.04566			12.910
	0.04541			14.244			0.04541			13.921			0.05125			13.117
	0.05096			14.524			0.05096			14.146			0.05683			13.288
	0.05650			14.755			0.05650			14.331			0.06241			13.431
	0.06205			14.950			0.06205			14.486			0.06800			13.553
	0.06759			15.117			0.06759			14.617			0.07358			13.658
	0.07313			15.262			0.07313			14.730			0.07916			13.750
	0.07868			15.389			0.07868			14.828			0.08475			13.831
	0.08422			15.501			0.08422			14.914			0.09033			13.903
	0.08977			15.601			0.08977			14.991			0.09591			13.967
	0.09531			15.691			0.09531			15.060			0.10150			14.024
	0.10086			15.773			0.10086			15.122			0.10708			14.076
	0.10640			15.847			0.10640			15.178			0.11266			14.123
	0.11195			15.916			0.11195			15.229			0.11825			14.166
	0.11749			15.978			0.11749			15.276			0.12383			14.206
	0.12304			16.036			0.12304			15.319			0.12941			14.242
	0.12858			16.090			0.12858			15.359			0.13500			14.275
	0.13412			16.139			0.13412			15.395			0.14058			14.306
	0.13967			16.186			0.13967			15.429			0.14616			14.335
	0.14521			16.229			0.14521			15.461			0.15075			14.357
	0.14970			16.262			0.14970			15.485						