s20nm_l600nm_4																
strain_X [-]	stress_X [MPa]	strain_Y [-]	stress_Y [MPa]	strain_Z [-]	stress_Z [MPa]											
	0.00000			0.000			0.00000			0.000			0.00000			0.000
	0.00055			0.513			0.00055			0.580			0.00056			0.529
	0.00111			1.024			0.00111			1.159			0.00112			1.057
	0.00194			1.784			0.00194			2.016			0.00195			1.839
	0.00319			2.889			0.00319			3.241			0.00321			2.992
	0.00506			4.420			0.00506			4.880			0.00509			4.629
	0.00787			6.295			0.00787			6.894			0.00792			6.679
	0.01067			7.691			0.01067			8.413			0.01075			8.202
	0.01348			8.742			0.01348			9.536			0.01357			9.345
	0.01769			9.894			0.01769			10.745			0.01781			10.554
	0.02323			10.930			0.02323			11.802			0.02205			11.388
	0.02878			11.639			0.02878			12.522			0.02629			11.997
	0.03432			12.148			0.03432			13.046			0.03188			12.583
	0.03987			12.531			0.03987			13.443			0.03746			13.017
	0.04541			12.830			0.04541			13.755			0.04305			13.350
	0.05096			13.072			0.05096			14.007			0.04863			13.615
	0.05650			13.272			0.05650			14.215			0.05421			13.831
	0.06205			13.441			0.06205			14.391			0.05980			14.012
	0.06759			13.586			0.06759			14.541			0.06538			14.165
	0.07313			13.711			0.07313			14.670			0.07096			14.298
	0.07868			13.821			0.07868			14.784			0.07655			14.413
	0.08422			13.918			0.08422			14.885			0.08213			14.516
	0.08977			14.005			0.08977			14.974			0.08771			14.607
	0.09531			14.084			0.09531			15.055			0.09330			14.688
	0.10086			14.155			0.10086			15.128			0.09888			14.761
	0.10640			14.219			0.10640			15.194			0.10446			14.828
	0.11195			14.278			0.11195			15.254			0.11005			14.888
	0.11749			14.332			0.11749			15.310			0.11563			14.944
	0.12304			14.382			0.12304			15.361			0.12121			14.995
	0.12858			14.428			0.12858			15.409			0.12680			15.042
	0.13412			14.471			0.13412			15.453			0.13238			15.086
	0.13967			14.511			0.13967			15.493			0.13796			15.126
	0.14521			14.548			0.14521			15.532			0.14355			15.164
	0.14970			14.577			0.14970			15.561			0.14913			15.199
																	0.15075			15.209