Interlaminar Fracture Energy of Laminates Made of Thermoplastic Impregnated Fiber Bundles
Citation Link: https://doi.org/10.15480/882.1612
Publikationstyp
Journal Article
Publikationsdatum
1988
Sprache
English
Enthalten in
Volume
1
Issue
3
Start Page
221
End Page
231
Citation
Journal of Thermoplastic Composite Materials 3 (1): 221-231 (1988)
Publisher DOI
Publisher
Sage
Interlaminar mode I- and II-fracture energy measurements (in terms of the strain energy
release rate) were carried out with different laminates of a glass fiber/thermoplastic PA 12-
and aramid fiber/PA 12-composite system. Specimens were prepared from fiber bundles
interspersed with polymer powder and a polymer sheath around them. The results, obtained
from two different test procedures and data reduction methods, reflect a good interlaminar fracture toughness of the different laminates. This can be attributed to the large damage zone size due to the tough matrix and a big amount of fiber bridging, which is highlighted by micrographs achieved with SEM-analysis.
release rate) were carried out with different laminates of a glass fiber/thermoplastic PA 12-
and aramid fiber/PA 12-composite system. Specimens were prepared from fiber bundles
interspersed with polymer powder and a polymer sheath around them. The results, obtained
from two different test procedures and data reduction methods, reflect a good interlaminar fracture toughness of the different laminates. This can be attributed to the large damage zone size due to the tough matrix and a big amount of fiber bridging, which is highlighted by micrographs achieved with SEM-analysis.