Titel: Effect of processing route on the microstructure and mechanical properties of hot work tool steel
Sprache: English
Autor/Autorin: Besler, Robert 
Bauer, Markus 
Furlan, Kaline Pagnan 
Klein, Aloisio Nelmo 
Janßen, Rolf 
Schlagwörter: powder metallurgy;steel;dilatometry;hardness measurement;mechanical characterization
Erscheinungsdatum: 21-Aug-2017
Verlag: Federal University of São Carlos, Department of Material Engineering ; Associação Brasileira de Metalurgia e Materiais (ABM), ABC, ABPol, SBCC, SBCr, SBMM ; SciELO
Quellenangabe: Materials Research 6 (20): 1518-1524 (2017)
Zeitschrift oder Schriftenreihe: Materials Research 
Zusammenfassung (englisch): Powder metallurgy is a growing sector in industrial production, as it offers outstanding energy, cost and material savings in comparison with established processing routes such as casting. Hot work toll steels are usually produced by ingot metallurgy, but also by powder metallurgy, namely hot isostatic pressing and powder forging routes. In this paper we investigate the possibility of production of a hot work tool steel (AISI H13) by conventional (die compaction and pressureless sintering) and metal injection molding routes, aiming to reduce cost and production time. The sintering behavior was studied from 1250 °C until 1430 °C and the resulting parts were compared in terms of microstructure, hardness and tensile strength. The results showed that both shaping routes together with pressureless sintering are suitable to produce this alloy. By combining the best shaping approach and a tailored sintering cycle, it was possible to produce samples with 400 HV10 as well as tensile strength of 1 GPa, which are comparable to the ones obtained by powder forging.
URI: http://hdl.handle.net/11420/2082
DOI: 10.15480/882.2078
ISSN: 1980-5373
Institut: Keramische Hochleistungswerkstoffe M-9 
Dokumenttyp: (wissenschaftlicher) Artikel
Enthalten in den Sammlungen:Publications (tub.dok)

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat
1516-1439-mr-1980-5373-MR-2016-0726.pdfVerlags-PDF1,37 MBAdobe PDFÖffnen/Anzeigen
Zur Langanzeige

Seitenansichten

25
checked on 23.03.2019

Download(s)

4
checked on 23.03.2019

Google ScholarTM

Prüfe

Export

Diese Ressource wurde unter folgender Copyright-Bestimmung veröffentlicht: Lizenz von Creative Commons Creative Commons