Title: R-curve behavior and flexural strength of zirconia-toughened alumina and partially stabilized zirconia composite laminates
Language: English
Authors: Blaese, Diego 
Benitez, Tobias 
Barros, Marcelo 
Jelitto, Hans 
Travitzky, Nahum 
Hotza, Dachamir 
Janßen, Rolf 
Issue Date: 15-Aug-2018
Source: Ceramics International 12 (44): 13463-13468 (2018-08-15)
Journal or Series Name: Ceramics international 
Abstract (english): A composite-laminate formed by thick layers ( 320 µm) of zirconia-toughened alumina (ZTA) with thin ( 50 µm) interlayers of zirconia partially stabilized (Y-PSZ) has been fabricated by tape casting and pressureless sintering. Fracture behavior and strength has been investigated and compared to a “monolithic” reference, e.g. a stack of zirconia-toughened alumina (ZTA) without interlayers. The fracture behavior has been analysed using stable crack growth in V-notched specimens loaded in 3-point bending. The ZTA+Y-PSZ composite laminate presented a rising crack resistance with maximum values between 6 and 14 MPa m1/2. In contrast, the “monolithic” ZTA laminate shows a plateau R-curve behavior at 2.7 MPa m1/2. Several toughening mechanisms were identified in the ZTA+Y-PSZ composite laminate, such as, crack arrest/slow down, micro cracking and bifurcation. These toughening mechanisms are most likely caused by high tensile residual stresses that were estimated theoretically.
URI: http://hdl.handle.net/11420/2844
ISSN: 0272-8842
Institute: Keramische Hochleistungswerkstoffe M-9 
Type: (wissenschaftlicher) Artikel
Appears in Collections:Publications without fulltext

Show full item record

Page view(s)

87
Last Week
0
Last month
5
checked on Sep 27, 2020

Google ScholarTM

Check

Add Files to Item

Note about this record

Export

Items in TORE are protected by copyright, with all rights reserved, unless otherwise indicated.