Title: Interfaces in metamict titanite : the macroscopic mechanical properties after stepwise annealing
Language: English
Authors: Beirau, Tobias 
Guglielmi, Paula O. 
Paulmann, Carsten 
Schneider, Gerold A. 
Groat, Lee A. 
Malcherek, Thomas 
Saljé, Ekhard K. Hermann 
Bismayer, Ulrich 
Keywords: Metamict;Nanoindentation;Synchrotron XRD;Titanite
Issue Date: 21-Jun-2012
Publisher: Taylor & Francis
Source: Phase Transitions 1 (86): 23-32 (2013)
Journal or Series Name: Phase transitions 
Abstract (english): Elastic material properties of metamict titanite (sample E2312) during thermally induced stepwise recrystallization are measured using nanoindentation. Changes of the elastic modulus (E) and the hardness (H) are related to increasing longrange order and vanishing amorphous interface areas. Metamict titanite shows H and E values close to titanite glass. H decreases on annealing until ca. 950 K. to 9.08 GPa and increases at higher temperatures, while E increases continuously on annealing up to ca. 168.4 GPa at 1220K. Crystalline titanite from Rauris shows strong anisotropy and H and E values are clearly larger than those of E2312. © 2013 Taylor & Francis.
ISSN: 0141-1594
Institute: Keramische Hochleistungswerkstoffe M-9 
Type: (wissenschaftlicher) Artikel
Funded by: Deutsche Forschungsgemeinschaft (DFG)
Appears in Collections:Publications without fulltext

Show full item record

Page view(s)

checked on Oct 25, 2020

Google ScholarTM


Add Files to Item

Note about this record


Items in TORE are protected by copyright, with all rights reserved, unless otherwise indicated.