Now showing1 - 2 of 2
- Some of the metrics are blocked by yourconsent settings
Item type:Publication, Access status: with files , Effects of hygrothermal ageing on the interphase, fatigue, and mechanical properties of glass fibre reinforced epoxy(Multidisciplinary Digital Publishing Institute (MDPI), 2019-06-14); ; ; Reliability and cost-effectiveness represent major challenges for the ongoing success of composites used in maritime applications. The development of large, load-bearing, and cyclically loaded structures, like rotor blades for wind or tidal energy turbines, requires consideration of environmental conditions in operation. In fact, the impact of moisture on composites cannot be neglected. As a result of difficult testing conditions, the knowledge concerning the influence of moisture on the fatigue life is limited. In this study, the impact of salt water on the fatigue behaviour of a glass fibre reinforced polymer (GFRP) has been investigated experimentally. To overcome the problem of invalid failure during fatigue testing, an improved specimen geometry has been developed. The results show a significant decrease in fatigue life for saturated GFRP specimens. In contrast, a water absorption of 50% of the maximum content showed no impact. This is especially remarkable because static material properties immediately decrease with the onset of moisture absorption. To identify the water absorption induced damage progress, light and scanning electron microscopy was used. As a result, the formation of debondings and cracks in the fibre-matrix interphase was detected in long-term conditioned specimens, although no mechanical loading was applied.Publicationtype: Journal ArticleScopus© Citations 33 288 326 - Some of the metrics are blocked by yourconsent settings
Item type:Publication, Access status: with files , Evaluation and modeling of the fatigue damage behavior of polymer composites at reversed cyclic loading(Multidisciplinary Digital Publishing Institute (MDPI), 2019-05-28); ; ; ; Understanding the composite damage formation process and its impact on mechanical properties is a key step towards further improvement of material and higher use. For its accelerated application, furthermore, practice-related modeling strategies are to be established. In this collaborative study, the damage behavior of carbon fiber-reinforced composites under cyclic loading with load reversals is analyzed experimentally and numerically. The differences of crack density evolution during constant amplitude and tension-compression block-loading is characterized with the help of fatigue tests on cross-ply laminates. For clarifying the evolving stress-strain behavior of the matrix during static and fatigue long-term loading, creep, and fatigue experiments with subsequent fracture tests on neat resin samples are applied. The local stress redistribution in the composite material is later evaluated numerically using composite representative volume element (RVE) and matrix models under consideration of viscoelasticity. The experimental and numerical work reveals the strong influence of residual stresses and the range of cyclic tension stresses to the damage behavior. On the microscopic level, stress redistribution dependent on the mean stress takes place and a tendency of the matrix towards embrittlement was found. Therefore, it is mandatory to consider stress amplitude and means stress as inseparable load characteristic for fatigue assessment, which additionally is influenced by production-related and time-dependent residual stresses. The phenomenological findings are incorporated to a numerical simulation framework on the layer level to provide an improved engineering tool for designing composite structures.Publicationtype: Journal ArticleScopus© Citations 18 354 404