Deformation of press-fitted metallic resurfacing cups. Part 1: Experimental simulation

The interference press fit of a metallic one-piece acetabular cup employed for metal-on-metal hip resurfacing procedures was investigated experimentally under laboratory conditions in the present study, in particular regarding the cup deformation. Tests were carried out in cadavers as well as polyurethane foams of various grades with different elastic moduli to represent different cancellous bone qualities. The cadaver test was used to establish the most suitable configuration of the foam model representing realistic support and geometrical conditions at the pelvis. It was found that a spherical cavity, with two identical areas relieved on opposite sides, was capable of creating a two-point pinching action of the ischeal and ilial columns on the cup as the worst-case scenario. Furthermore, the cup deformation produced from such a two-point loading model with a grade 30 foam was similar to that measured from the cadaver test. Therefore, such a protocol was employed in subsequent experimental tests. For a given size of the outside diameter of the cup of 60 mm, the cup deflection was shown to be dependent largely on the cup wall thickness and the diametral interference between cup and prepared cavity at implantation. For a relatively thin cup with a wall thickness between 2.3 mm (equator) and 4 mm (pole) and with a modest nominal diametral interference of 1 mm, which corresponds to an actual interference of approximately 0.5 mm, the maximum diametral cup deflection (at the rim) was around 60 microm, compared with a diametral clearance of 80-120 microm between the femoral head and the acetabular cup, generally required for fluid-film lubrication and tribological performances. Stiffening of the cup, by both thickening and lateralizing by 1 mm, reduced the cup deformation to between 30 and 50 microm with actual diametral interferences between 0.5 and 1 mm.

Subjects

Arthroplasty, Replacement, Hip

Biocompatible Materials

Cadaver

Elasticity

Equipment Design

Equipment Failure Analysis

Hardness

Hardness Tests

Humans

In Vitro Techniques

Materials Testing

Metals

Pressure

Prosthesis Design

Surface Properties

Hip Prosthesis

Prosthesis Failure

DDC Class

610: Medizin

Lizenz

http://rightsstatements.org/vocab/InC/1.0/

Name

095441105x69150.pdf

Size

323.1 KB

Format

Adobe PDF

Options

Deformation of press-fitted metallic resurfacing cups. Part 1: Experimental simulation