3 results
Now showing1 - 3 of 3
- Some of the metrics are blocked by yourconsent settings
Item type:Publication, Access status: without files , Valorization of waste lavender residue from the essential oil industry for production of rosmarinic acid - a study on the solid-liquid extractionThe possibility for valorization of the waste lavender residue from the essential oil industry via solvent extraction was studied. The plant residue of Lavandula angustifolia, from which the lavender oil is extracted through steam distillation, contains Key Biologically Active Components (KBAC) such as: rosmarinic acid, caffeic acid, luteolin. The feasibility of the solvent extraction for their isolation was assessed by comparison of the kinetics and equilibrium of extraction of KBAC from spent and raw plant material (collected from the same batch before the steam distillation) using different solvent compositions. The parameters of the extraction process were experimentally and numerically optimized. To determine the most efficient solvent, two pure and two mixed solvents were tested: pure water, 99.9 % ethanol and their mixtures - (40 % and 60 % ethanol). Using 40 % ethanol as extraction solvent resulted in maximum recovery of KBAC. A mathematical model for the solid-liquid extraction from lavender materials was developed. The values of the model parameters were determined using the Regular regime method. A four-parameter empirical model for prediction of the effective diffusivity, Deff, was also applied. The model adequacy was experimentally verified. Based on the theoretical and experimental results KBAC recovery the following extraction conditions were recommended: extraction time - 30 min, temperature - 30 °C, liquid-solid ratio - 0,01 m3 kg- and 40 % ethanol as an extraction solvent.Publicationtype: Journal Article67 - Some of the metrics are blocked by yourconsent settings
Item type:Publication, Access status: with files , Spray coating of cellulose aerogel particles in a miniaturized spouted bed(Springer, 2021-07-04); ; ; ; Aim of this work is to apply protective and homogeneous shellac coating layers on the surface of hydrophilic open-pore cellulose aerogel particles with low densities ≤ 0.1 g/cm3 and high specific surface areas in the range of ~ 400–450 m2/g while keeping the aerogels’ microstructure intact during processing. For this purpose, an innovative miniaturized spouted bed setup was used. Successful process settings for application of enclosed films on aerogel surfaces without intrusion of coating material into the pores were determined. Precise control of coating layer thickness in the range of 10–50 µm was achieved due to variation of coating solution amount without agglomeration and clogging events occurring during processing. Comparison of bulk densities and specific surface areas before and after coating proved the intactness of the porous structure. Coating of particles loaded with vanillin led to controlled release, enhancing release half-life times from 20 to 1600 min. Overall, a successful strategy for coating of organic low-density aerogels was developed.Publicationtype: Journal ArticleScopus© Citations 13 219 261 - Some of the metrics are blocked by yourconsent settings
Item type:Publication, Access status: with files , Cellulose aerogel particles: control of particle and textural properties in jet cutting process(Springer, 2021-01); ; ; ; Reported approach aims for the synthesis of spherical cellulose beads with high production rates (0.7–4.1 kg/h of hydrogel) via the so-called jet cutting method. To form particles, jets of aqueous cellulose/sodium hydroxide solutions were cut into pieces and collected in a gelation bath (30 wt% aqueous H2SO4, 20 °C). After solvent exchange with ethanol and subsequent supercritical drying, cellulose aerogel particles were obtained. The particles showed high specific surface areas (ca. 400 m2/g) and low bulk (untapped) densities (0.06–0.10 g/cm3). Variation of cellulose content (4–7 wt%) and jet cutting process parameters (cutting frequency, nozzle diameter, jet velocity) turned to be useful parameters for controlling the particles size and shape. Highly spherical particles with sphericity SPH ≥ 0.92 were obtained in a broad range of achievable particle sizes (0.4–1.0 mm), with an optimum of SPH at 6 wt% cellulose content.Publicationtype: Journal ArticleScopus© Citations 16 270 387